Browse by
Continent
Outer(Air)Layer
Mid Layer
Inner(Cell)Layer
Tensile Strength(Width/TD) ≥
Mpa
Interlayer Peel Strength ≥
N/cm
Thermal Shrinkage(Width/TD) ≤
%
Elongation(Length/MD) ≥
%
Elongation(Width/TD) ≥
%
Partial Discharge Voltage ≥
VDC
Breakdown Voltage ≥
kV
MVTR ≤
g/m2 per day
Width ≥
mm
Weight ≤
g/m2
Solar Backsheet Directory
(139 Individual Backsheet Models)
Backsheet Filters
%
-
Layers: PET / PET / Primer Tensile Strength: 100 MPa Total Thickness: 360±5 µm Thermal Shrinkage: ≤ 1.5 % Region: India 
-
Layers: PVDF / PET / EVA Tensile Strength: 128 MPa Total Thickness: 300±50 µm Thermal Shrinkage: ≤ -- Region: China 
-
Layers: Coating / PET / Coating Tensile Strength: 160 MPa Total Thickness: 253±12.65 µm Thermal Shrinkage: ≤ 1 % Region: China
-
Layers: PVF / PET / PE Tensile Strength: 120 MPa Total Thickness: 287±14.35 µm Thermal Shrinkage: ≤ 1 % Region: China
-
Layers: PET Tensile Strength: 120 MPa Total Thickness: 406±20.3 µm Thermal Shrinkage: ≤ 0.6 % Region: China
Pv backsheets are made by composite of eva adhesive layer made of BR film
Support layer made of weather resistant pet and intermediate layer made of water vapor barrier film
-
Layers: EVA / PET / PVDF Tensile Strength: 140 MPa Total Thickness: 300±20 µm Thermal Shrinkage: ≤ -- Region: China
-
Layers: PVDF / PET / EVA Tensile Strength: 81 MPa Total Thickness: 328±32.8 µm Thermal Shrinkage: ≤ 1.5 % Region: United States 
-
Layers: Polyolefin / Polyolefin / Polyolefin Tensile Strength: 83 MPa Total Thickness: 250±10 µm Thermal Shrinkage: ≤ 0.3 % Region: Germany 
-
Layers: PVDF / PET Tensile Strength: 120 MPa Total Thickness: 284±14.2 µm Thermal Shrinkage: ≤ 1 % Region: China
-
Layers: PET Tensile Strength: 120 MPa Total Thickness: 288±14.4 µm Thermal Shrinkage: ≤ 1 % Region: China